Material performance of PP-H
Source:    Publish Time: 2015-09-06 21:30   351 Views   Size:  16px  14px  12px

PP-H is a modified polypropylene material, it has been β modified with delicate crystalline structure, not only has excellent chemical resistance, temperature resistance and good creep resistance, also has excellent impact resistance at low temperatures. it increased hydrostatic strength, enhanced chemical resistance. 


According to the characteristics of PP-H materials, the products and equipment made by PP-H pipe and sheet are widely used in corrosive and chemical, metallurgy and electronics industrial. the pickling tank and electrolyzer made by PP-H is economical and durable, reduce equipment maintenance, and extend the service life, with superior performance.



Beta(β)-PP BE60-7032 (PP-H) PROPERTY INDEX

 

Property                                                                    Test Method                  Typical Value  

Density                                                                            905 kg/m3                       ISO 1183

Melt Flow Rate(230/2.16kg)                                    0.30 g/10min                   ISO 1133

Melt Flow Rate(190/5.0kg)                                       0.50 g/10min                  ISO 1133

Tensile Modulus(1 mm/min)                                      1.300 Mpa                       ISO 527

Tensile Strain at Yield (50 mm/min)                          10%                                 ISO 527-2

Tensile Stress at Yield (50 mm/min)                         30 Mpa                            ISO 527-2

Heat Deflection Temperature                                      96℃                                 ISO 75-2

Vicat softening temperature B50, (50N)                    91℃                                 ISO 306

Charpy Impact Strength, notched (23℃)                 50kJ/m2                          ISO 179/1eA

Charpy Impact Strength, notched (-20℃)                5kJ/m2                            ISO 179/1eA